DECOSTONE GRANITE TILE AND CERAMIC ADHESIVE 25.KG (LARGE)
4.51$
MADE IN TURKEY
Prices are in American Dollar
Shipping prices not included
Prices are Exwork
- Description
- More Products
Description
DEFINITION:
It is a cement-based, large-size coating material adhesive mortar, such as granite, ceramic, marble, natural stone, porcelain, with high adhesion strength and high elasticity, reduced slip and extended working time.
Product Class: C2TE S1
APPLICATION AREAS AND PREPARATIONS:
• It can be used safely on the floors and walls of places such as hospitals, schools, stores, markets, which are exposed to heavy traffic indoors and outdoors.
APPLICATION:
• DECOTILE-101 GRANITE, TILE AND CERAMIC ADHESIVE-LARGE is added slowly into clean cold water and mixed with a low-speed mixer for 5-10 minutes until it becomes lump-free. The required amount of water is 25 kg. for 5.5-6.5 liters. The amount of water should be adjusted within these ratios according to the weather conditions. The mixed mortar is left for 5 minutes and mixed again.
• The prepared mixture is spread on the surface with a suitable trowel. According to the size of the material to be laid, suitable carding is done (one-sided or double-sided bonding) and the material is laid on the surface with the help of a rubber mallet. 24 hours after the application, the joint gaps are filled.
• If the surface and ambient temperature rises above +25oC, the surface and ceramics should be moistened by spraying at regular intervals to prevent sudden drying of the adhesive.
• Do not use by adding water to hardened and solidified material. Tools used after the application are cleaned with water immediately.
DECOSTONE Construction Chemicals Ltd. Sti. is not responsible.
TECHNICIAL SPECIFICATIONS:
• Appearance / Color: Gray Powder
• Density: 1.50±0.2 kg/lt
• Flexural Strength: >5 N/mm²
• Compressive Strength: >8 N/mm²
• Initial Tensile Adhesion: ≥ 1 N/mm²
• Tensile Adhesion Force After Immersion: ≥ 1 N/mm²
• Tensile Adhesion Force after Heat Aging: ≥ 1 N/mm²
• Tensile Adhesion Force After Freeze-Thaw Cycles: ≥ 1 N/mm²
• Open Waiting Time: Tensile Adhesion Force: ≥ 1 N/mm² (After min. 20 min.)
• Flexibility (12002): ≥ 2.5 mm – Flexible S1
It is produced in accordance with TS EN 12004 C2TE S1.
CONSUMPTION:
Depending on the surface and application conditions (one-sided or double-sided bonding), it is 4-7 kg/m².
PACKAGING:
25 kg Kraft Bag.
64 pieces, 1600 kg in 8-layer stacked pallets.
Pallet size: 110 cm x 110 cm.